里氏硬度法评估套筒灌浆料抗压强度研究
发布时间:2020-04-03 22:44:30      来源:未知
  摘要:为研究装配式建筑中钢筋套筒连接灌浆料强度的无损检测技术,设计制作了4组不同强度的套筒灌浆料试件并进行表面里氏硬度和抗压强度试验。结果表明:套筒灌浆料标准试件表面里氏硬度较好地服从正态分布;两次测试或对称侧面测试的结果具有重复性;通过拟定的数据处理方法,里氏硬度离散性显著减小,偏差在±20HL;灌浆料表面里氏硬度与其抗压强度具有显著相关性,其中采用指数回归拟合综合效果最好。研究结果为现场采用里氏法检测评估套筒灌浆料实体的强度提供了依据。

  关键词:套筒;灌浆料;无损检测;里氏硬度;抗压强度

  Study on the Evaluation of  Compressive Strength of Grouting Materials for Sleeves by Using Leeb Hardness Method

  Abstract:To find out a proper nondestructive test technology of the strength of grouting materials for steel sleeves in prefabricated building, four groups of grouting materials with different strength at different curing ages were designed and their strength was tested using surface Leeb hardness method. It is revealed the results from the surface Leeb hardness method of standard specimens obey normal distribution well. The results are founded to have good repeatability. Data processing showed that the deviation of Leed hardness was basically within ±20HL. There existed a significant correlation between the surface Leed hardness and the compressive strength of grouting material, among which the exponential regression fitted well. The results of this paper will provide reliable on-situ test method to evaluate compressive strength of grouting in sleeves based on Leeb hardness methodology.
Keywords:steel sleeves;grouting  materials;nondestructive test;Leeb hardness;compressive strength

0 引言

  在装配式混凝土结构中,钢筋套筒灌浆连接是一种常用的节点连接形式[1]。套筒灌浆料作为不同构件荷载传递的媒介,其强度是保证节点连接可靠性的关键因素[2]。然而,在实际施工中,常出现增大用水量以增强流动性或为了节省成本使用过期灌浆料,致使灌浆料抗压强度降低,严重影响连接性能,对整个建筑结构埋下严重安全隐患。

  由于套筒位于预制构件内,灌浆料隐蔽于套筒中,检测仪器无法直接与其接触,因此目前尚无有效手段可对套筒灌浆料实体强度进行检测。孙彬等[3]提出了利用灌浆孔道或出浆孔道PVC管内的灌浆料制作成圆柱体小芯样并进行抗压试验,利用换算公式得出套筒灌浆料标准试件的抗压强度的方法。由于小芯样与标准试件的换算公式需要通过大量试验获得且小芯样的抗压强度离散性较大,因此该方法仍然处于研究阶段。


  完整版请点击:CF38 里氏硬度法评估套筒灌浆料抗压强度研究.pdf